SS904L BAR SPECIFICATIONS
SS DIN 1.4539 Bars, Steel 904L Flat Bar, 904L Steel Hollow Bars, ASTM B649 Stainless Steel 904L Round Bars, 904L Stainless Steel Black Bar 904 L is completely austenitic and is less delicate to precipitation ferrite and sigma stages than customary austenitic evaluations with high molybdenum content. Typically, because of the blend of moderately high substance of chromium, nickel, molybdenum and copper 904L has great imperviousness to general consumption, especially in sulfuric and phosphoric conditions
904L is a high-combination austenitic stainless steel with low carbon content. The evaluation is expected for use under extreme destructive conditions. It has been application demonstrated over numerous years and was initially created to oppose erosion in weaken sulfuric corrosive.
| STAINLESS STEEL 904L SHEET, PLATE & COIL SPECIFICATIONS | ||
| Specifications | : | ASTM B625 / ASME SB625 |
| Thickness | : | 4mm-100mm |
| Width | : | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
| Length | : | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc |
| Surface | : | 2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc |
| Finish | : | Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
| Form | : | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc. |
SS904L PIPES,SHEETS AND PLATES
CHEMICAL COMPOSITION
| Grade | C | Cr | Cu | Mn | Mo | Ni | P | S | Si |
|---|---|---|---|---|---|---|---|---|---|
| 904L | Max | Max | Max | Max | Max | ||||
| 904L | 0.02 | 19.0-23.0 | 1.0-2.0 | 2.0 | 4.0-5.0 | 23.0-28.0 | 0.045 | 0.035 | 1.0 |
MECHANICAL PROPERTIES
| Density | 8.0 g/cm3 |
|---|---|
| Melting Point | 1454 °C (2650 °F) |
| Tensile Strength | Psi – 75000 , MPa – 515 |
| Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
| Elongation | 35 % |